Buy DIN EN E: CHARPY IMPACT TEST ON METALLIC MATERIALS – TEST METHOD from SAI Global. Purchase your copy of BS EN as a PDF download or hard copy directly from the official BSI Shop. All BSI British Standards. Find the most up-to-date version of DIN EN at Engineering
|Published (Last):||9 January 2013|
|PDF File Size:||1.63 Mb|
|ePub File Size:||8.80 Mb|
|Price:||Free* [*Free Regsitration Required]|
BS EN 10045-1:1990
1045-1 Brief history Foreword 1 Object and field of application 2 References 3 Principle ej Designations 5 Test pieces 6 Testing machine 7 Test requirements 8 Test report Annex A List of national standards corresponding to the reference European Standard in preparation Figure 1 — Charpy impact test Figure 2 — Configuration of test piece supports and anvils Table 1 — Designations Table 2 — Tolerances on specified test piece dimensions Table 3 — Characteristics of testing machine Table 4 — National standards corresponding to proposed European Standard Page 2 2 3 3 3 3 3 3 5 5 8 6 7 3 4 5 8 Foreword The standard EN 10 concerns metallic materials — Charpy impact test and comprises the following parts: Customers who bought this product also bought BS EN Essais de flexion par choc sur eprouvette Charpy.
General, tolerances and deviations. The values of the principal characteristics of the testing machine are specified in Table 3.
In the centre of the length, there shall be a notch. There is no general method for converting the results obtained by one test method into the values which would be obtained by another test method. For certain particular metallic materials and applications, the Charpy impact test may be the subject of specific standards and particular requirements.
Methode d’essai Title in German Metallische Werkstoffe. Worldwide Standards We can source any standard from anywhere in the world.
Click to learn more. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the CEN Central Secretariat or to any CEN 10054-1.
Verification of pendulum impact testing machines. The test pieces shall be machined all over, except in the case of precision cast foundry test pieces in which the two faces parallel to the plane of symmetry of the notch can be unmachined.
Take the smart route to manage medical device compliance. October Replaced By: The faster, easier way to work with standards. For certain particular metallic materials and applications, the Charpy impact test may be the subject of specific standards and particular requirements.
Please download Chrome or Firefox or view our browser tips. The reported absorbed energy under these conditions shall be designated by the symbols: You may experience issues viewing this site in Internet Explorer 9, 10 or This absorbed energy is a measure of the impact strength of the material.
The test piece may be marked on any face not in contact with the supports or anvils and at a point at least 5 mm from the notch to avoid the effects of cold working due to marking.
The test piece shall be broken within 5 seconds of the time of removal from the medium. The test consists of breaking by one blow from a swinging pendulum, under defined conditions, a test piece notched in the middle and supported at each end. NOTE It is emphasized that only results on test pieces of identical dimensions should be compared.
EN Impact Test_百度文库
Find Similar Items This product falls into the following categories. Your basket diin empty. Metal products, mechanical tests, Charpy impact tests, test specimens, testing conditions. Accept and continue Learn more about the cookies we use and how to change your settings.
If standard test pieces cannot be obtained from the material, a reduced section test piece, with a width of 7,5 mm or 5 mm see Table 2 ddin be used, the notch being cut in one of the narrow faces. This absorbed energy is a measure of the impact strength of the material.
Part 4 ej, BS Until this European Standard is published reference can be made to the corresponding national or international standards, a list of which is given in annex A.
Metallic materials — Impact test. The transfer device shall be designed and used in such a way that the temperature of the test piece is maintained within the temperature range permitted. Comparison of results, however, is only of significance when made between test pieces of the same form and dimensions. The energy absorbed is determined in joules.
A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to CEN Central Secretariat has the same status as the official versions.
EU, Impact testing using V-notch, beam type test piece. The test report shall state that the test piece 100445-1 not broken by x J. This website is best viewed with browser version of up to Microsoft Internet Explorer 8 or Firefox 3.
The energy absorbed is determined in joules. For tests at temperatures other than ambient, the test piece shall be immersed in the cooling or heating medium for sufficient time to ensure that the required temperature is reached throughout the test piece for example, at least 10 min in a liquid medium or at least 30 min in a gaseous medium. Search all products by.